Does Addition of Propolis to Glass Ionomer Cement Alter its Physicomechanical Properties? An In Vitro Study

Propolis is a natural resinous substance produced by honey bees. The antimicrobial effects of glass ionomer cement have been shown to improve with the addition of propolis; however its effect on the physicomechanical properties of the cement is not known. Aim: The purpose of this study was to evaluate the compressive strength and solubility of conventional restorative glass ionomer cement following the addition of propolis. Study design: Twenty half cylindrical samples were prepared with conventional restorative glass ionomer cement formed the control group. Another twenty samples were prepared with propolis added to conventional restorative glass ionomer cement formed the experimental group. The compressive strength was assessed using universal testing machine. To assess solubility, the samples were immersed in deionised water at room temperature, for 7 days. The solubility was measured as a difference in the weight of the sample; prior to immersion and following immersion at the end of each day. Results: The control group had a significantly higher mean compressive strength of 146.26 Mpa as compared to the experimental group (135.06 Mpa). The solubility between the groups was significant. Conclusion: In comparison to the control group, incorporation of propolis to conventional restorative glass ionomer cement decreased the compressive strength significantly. The solubility of the cement in the experimental group increased significantly over 7day period as compared to the control group.

glass ionomer cement, propolis, compressive strength, solubility

1. Wilson AD, McLean JW. Glass ionomer cement. Chicago: Quintessence Publ Co, 1988:1- 4.

2. Yap AUJ, Cheang PH, Chay PL. Mechanical properties of two restorative reinforced glass-ionomer cements. J Oral Rehabil. 2002; 29(7):682-8

3. Hse KM, Leung SK, Wei SH. Resin-ionomer restorative materials for children: a review. Aust Dent J. 1999; 44(1):1-11.

4. Takahashi Y, Imazato S, Kaneshiro AV, Ebisu S, Frecken JE, Tay FR. Antibacterial effects and physical properties of glass ionomer cement containing chlorhexidine for the ART approach. Dent Mater. 2006; 22:647-52

5. Yesilyurt C, Er K, Tasdemir T, Buruk K, Celik D. Antibacterial activity and physical properties of glass-ionomer cements containing antibiotics. Oper Dent. 2009; 34(1):18-23

6. Al Zraikat H, Palamara JE, Messer HH, Burrow MF, Reynolds EC. The incorporation of casein phosphopeptide-amorphous calcium phosphate into glass ionomer cement. Dent mater. 2011; 27(3):235-43

7. Kumazawa S, Hamasaka T, Nakayama T. Antioxidant activity of propolis of various geographic origins. Food Chem. 2004; 84:329–339.

8. Topcuoglu N, Ozan F, Ozyurt M, Kulekci G. In vitro antibacterial effects of glass-ionomer cement containing ethanolic extract of propolis on Streptococcusmutans. Eur J Dent. 2012; 6(4):428-33

9. International Organization for standardization. ISO9917. Dental glass polyalkenoate cements. Geneva; ISO 9917-2:2010

10. Vassya Bankova. Recent trends and important developments in propolis research. eCAM. 2005; 2(1) 29-32

11. Da Silva FB, De Almeida JM, De Sousa SMG. Natural medicaments inendodontics-a comparative study of the anti inflammatory action. Braz Oral Res. 2004; 18(2):174-9

12. Yap AUJ, Pek YS, Cheang P. Physicomechanical properties of a fast set highly viscous GIC restorative cement. J Oral Rehabil. 2003; 30:1-8

13.Toledano M, Osorio R, Osorio E, Fuentes V, Prati C, Garcia-Godoy F. Sorption and solubility of resin-based restorative dental materials, J Dent. 2003; 31(1):43-50.

14. Hatunoglua E, Ozturkb F, Bilenlerc T, Aksakallıd S, Simseke N. Antibacterial and mechanical properties of propolis added to glass ionomer cement. Angle Orthod. 2014;84:368–373.

15.Troca VBPB, Fernandes KBP, Terrile AE, Marcucci MC, de Andrade FB, Wang LD. Effect of green propolis addition to physical-mechanical properties of glass ionomer cements. J Appl Oral Sci. 2011;19:100–105.